DATASHEET | VALUE | UNIT | TEST CONDITIONS | TEST METHOD |
Density | ۰.۹۲۱ | g/cm³ | ISO 1183 | |
MFI | ۰.۳ | g/10min | ۲.16Kg , 190°C | ASTM D1238 |
Blocking | ۰.۷ | |||
Dart Drop Impact Strength | ۳۵ | KJ/m | ASTM D1894 | |
Film Elongation at Break, MD | ۲۰۰ | % | ASTM D4272 | |
Film Elongation at Break, TD | ۵۰۰ | % | ISO 527 | |
Film Tensile Modulus, MD | ۱۸۰ | MPa | ISO 527 | |
Film Tensile Modulus, TD | ۱۹۰ | MPa | ISO 527 | |
Film Tensile Strength at Break, MD | ۲۹ | MPa | ISO 527 | |
Film Tensile Strength at Break, TD | ۲۶ | MPa | ISO 527 | |
Film Tensile Strength at Yield, MD | ۱۲ | MPa | ISO 527 | |
Film Tensile Strength at Yield, TD | ۱۱ | MPa | ISO 527 | |
Re-Blocking | ۳۰ | gr | ||
Tear Strength, MD | ۲۰ | kN/m | ISO 6383 | |
Tear Strength, TD | ۲۵ | kN/m | ISO 6383 | |
Gloss | ۴۶ | ۴۵ ° | ASTM D2457 | |
Haze | ۱۲ | % | ASTM D1003 |
– Manufacturer: Laleh Pet.co.
– Application: shrink hoods, industrial sacks, heavy duty carrier bags and liners.
– Process: Blown film.
– Features: Good rigidity, High molecular weight, Good tear strength, Good tensile strength, Good dimensional stability.