DATASHEET | VALUE | UNIT | TEST CONDITIONS | TEST METHOD |
Density | ۰.۹۲۳ | g/cm³ | ISO 1183 | |
MFI | ۰.۲۵ | g/10min | At 2.16Kg /190°C | ISO 1133 |
Film Elongation at Break, MD | ۲۰۰ | % | ISO 527 | |
Film Elongation at Break, TD | ۵۰۰ | % | ISO 527 | |
Film Tensile Strength at Break, MD | ۲۷ | MPa | ISO 527 | |
Film Tensile Strength at Break, TD | ۲۰ | MPa | ISO 527 | |
Impact Strength, Dart | ۲۵۰ | gr | ۵۰µ Blown film | ASTM D1709 |
Tensile Modulus | ۲۴۰ | MPa | ISO 527 | |
Tensile Strength at Yield | ۱۰ | MPa | ISO 527 | |
Vicat Softening Point | ۹۴ | °C | ۵۰°C/h, 10N | ISO 306 |
Gloss | ۵۰ | ۶۰°/۵۰µ Blown film | ASTM D2457 | |
Haze | ۱۴ | % | ۵۰ , < 14 | ASTM D1003 |
– Manufacturer: Amirkabir Pet.co.
– Application: Bottles, Film, Shiring Film, Bags, General-purpose film.
– Process: Blown film, Injection Molding, Blow Molding
– Features: Good processability, Good tear strength, Good toughness.